Neoprene Gaskets

Neoprene Rubber Gaskets

Select your desired material grade from our options below. If you need assistance choosing the most appropriate material grade or are looking for something not listed, please contact us.

Choose from a selection of default gasket designs, or upload your custom gasket design with any additional requirements.

Technical data for each material is available below.

Images are used for illustration purposes. The final colours may not exactly reflect per the images shown and thicknesses will vary per your requirements. Please contact us for more information.

Choose Your Gasket

Gasket Design Options

Circular Gasket/Washer
Solid Disc
Circular Gasket with Holes
Circular/Flange Gasket with Holes
Square/Rectangular Gasket
Solid Square/Rectangular
Square/Rectangular Gasket with Holes
Square/Rectangular, Square Centre with Holes
Square/Rectangular, Circular Centre
Square/Rectangular, Circular Centre with Holes
Flange Gasket
Rubber Strip
Custom Gasket
  • White Food Quality FDA Approved Neoprene
  • Neoprene/SBR 1-ply Insertion Rubber
  • High Grade Reinforced Coated Nylon Neoprene
  • High Grade Non-reinforced Diaphragm Neoprene
  • Flame Retardant NFF16-101 M2-F3 UL94-VO Neoprene
  • Flame Retardant ISO 0340 Neoprene
  • INTERNATIONAL MARITIME ORGANISATION (IMO) FTP CODE PART 5/ISO 5658-2:2006 IMO Compliant, Grey Flame Retardant Neoprene 70° Shore
  • Commercial Quality Soft Neoprene/SBR
  • BS2752 C80 Neoprene
  • BS2752 C70 Neoprene
  • BS2752 C60 Neoprene
  • BS2752 C50 Neoprene
  • BS2752 C40 Neoprene
  • Blue Metal Detectable FDA Approved Neoprene
  • 30% Content Neoprene/SBR
  • 10% Content Neoprene/SBR
View Material ProductDownload Data Sheet
  • Approved to: US FDA21 CFR177,2600,EU1935/2004
  • USP Class V1 Compliant
  • Food Quality Neoprene: 65° Shore
  • White – RAL 1015
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.60 ± 0.05 ASTM D297 1.60 ± 0.05
HARDNESS DIN 53505 65 ± 5 SH A ASTM D2240 65 ± 5 SH A
TENSILE STRENGTH ( MIN ) DIN 53504 716 PSI ASTM D412 50 KG/CM2
ELONGATION AT BREAK ( MIN ) DIN 53504 250 ASTM D412 250
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) DIN ISO 815-1 30 ASTM D395 METHOD B 30
TEAR RESISTANCE ( ANGULAR ) MIN DIN 53515 196 LBS/INCH ASTM D624 35 KG/CM
CHANGE IN PROPERTIES
HEAT AGEING ( 72 HRS. AT 70 ºC ) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 15 + 10 / – 15
— ELONGATION AT BREAK (%) + 10 / – 20 + 10 / – 20
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 + 2 % + 2 %
IRM OIL NO.2 + 15% + 15%
IRM OIL NO.3 + 45% + 45%
POLYMER CONTENT (NEOPRENE) 100% 100%
CHEMICAL RESISTANCE
— OZONE FAIR ASTM D 1149 FAIR
— DILUTE ACIDS AND BASES GOOD GOOD
— CONCENTRATED ACIDS AND BASES FAIR FAIR
— OILS GOOD GOOD
— SOLVENTS FAIR FAIR
TEMPERATURE RANGE -30º TO + 130º C -30º TO + 130º C
COLOUR WHITE – RAL 1015
View Material ProductDownload Data Sheet
  • REACH, RoHS, PAH and CE compliant
  • For use with commercial quality applications
  • SBR blend with a 1 ply 22gsm cotton fabric reinforcement: 70° Shore
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.45 ± 0.05 ASTM D297 1.45 ± 0.05
HARDNESS DIN 53505 70 ± 5 SH A ASTM D2240 70 ± 5 SH A
TENSILE STRENGTH (MIN) DIN 53504 569 PSI ASTM D412 40 KG/CM2
ELONGATION AT BREAK (MIN) DIN 53504 200% ASTM D412 200%
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) DIN ISO 815-1 40% ASTM D395 METHOD B 40%
TEAR RESISTANCE (ANGULAR) MIN DIN 53515 100 LBS/INCH ASTM D624 18 KG/CM
CHANGE IN PROPERTIES
HEAT AGEING (72 HRS. AT 70ºC) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 25 + 10 / – 25
— ELONGATION AT BREAK (%) + 10 / – 25 + 10 / – 25
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 + 33% + 33%
IRM OIL NO.2 + 47% + 47%
IRM OIL NO.3 + 90% + 90%
POLYMER CONTENT (NEOPRENE) 10% 10%
CHEMICAL RESISTANCE
— OZONE FAIR ASTM D 1149 FAIR
— DILUTE ACIDS AND BASES FAIR FAIR
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED NOT RECOMMENDED
— OILS NOT RECOMMENDED NOT RECOMMENDED
— SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE -30 º TO +90º C -30 º TO +90º C
COLOUR BLACK
INSERTION 1 PLY 22GSM COTTON FABRIC INSERTION
View Material ProductDownload Data Sheet
  • Generally conforms to BS2752-C60
  • REACH, RoHS, PAH and CE compliant
  • 1 ply 150 GSM Nylon: 60° Shore
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.30
HARDNESS BS 903: PART A26 60 ± 5 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 130
ELONGATION AT BREAK (MIN) BS 903: PART A2 350%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 25%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 35 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 70% (MAX)
RESISTANCE TO LOW TEMPERATURE AT –

40ºC

 BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC &

NAPHTHANIC HC

 GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
INSERTION 1PLY 150GSM Nylon fabric reinforcement
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +70
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • REACH, RoHS, PAH and CE compliant
  • Good resistance to oil, fuel and certain chemicals
  • Non-Reinforced Diaphragm, High Grade Neoprene: 60° Shore
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.40±0.05 ASTM D297 1.40±0.05
HARDNESS DIN 53505 65 ± 5 SH A ASTM D2240 65 ± 5 SH A
TENSILE STRENGTH (MIN) DIN 53504 1422 PSI ASTM D412 100 KG/CM2
ELONGATION AT BREAK (MIN) DIN 53504 400 % ASTM D412 400 %
COMPRESSION SET (70ºC/24 HRS/25% COMPRESSION) (MAX) DIN ISO 815-1 40% ASTM D395 METHOD B 40%
TEAR RESISTANCE (ANGULAR) MIN DIN 53515 95 LBS/INCH ASTM D624 25 KG/CM
CHANGE IN PROPERTIES AFTER
HEAT AGEING FOR (72 HRS. AT 70ºC ) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 25 + 10 / – 25
— ELONGATION AT BREAK (%) + 10 / – 30 + 10 / – 30
VOLUME SWELL: AT 70º C FOR 72 HRS ASTM D 471
IN IRM OIL NO.1 + 18% + 18%
IN IRM OIL NO.2 + 23% + 23%
IN IRM OIL NO.3 + 60% + 60%
POLYMER CONTENT (NEOPRENE) 100% 100%
CHEMICAL RESISTANCE
— OZONE GOOD ASTM D 1149 GOOD
— DILUTE ACIDS AND BASES FAIR FAIR
— CONCENTRATED ACIDS AND BASES FAIR FAIR
— OILS GOOD GOOD
— SOLVENTS FAIR FAIR
TEMPERATURE RANGE -30º TO + 130º C -30º TO + 130º C
View Material ProductDownload Data Sheet
  • Fire Resistance to: NFF16-101 M2-F3 & DIN75200-UL94VO
  • REACH, RoHS, PAH and CE compliant
  • Chloroprene, Neoprene compound: 65° Shore
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY 1.60 ± 0.05 ASTM D297 1.60 ± 0.05
HARDNESS ISO 48-4 65 ± 5 SH A ASTM D2240 65 ± 5 SH A
TENSILE STRENGTH (MIN) ISO 37 711 PSI ASTM D412 50 KG/CM2
ELONGATION AT BREAK (MIN) ISO 37 200% ASTM D142 200%
COMPRESSION SET (70°C/24h/25% compression) (max) ISO 815-1 50% ASTM D395 Method B 50%
TEAR RESISTANCE (ANGULAR) MIN ISO 34-1 112 LBS/INCH ASTM D624 20Kg/cm
CHANGE IN PROPERTIES AFTER
HEAT AGEING FOR (72 hrs. AT 70°C) ASTM D573
–HARDNESS (Pts) +5(Max) +5(Max)
–TENSILE STRENGTH (%) +10/-20 +10/-20
ELONGATION AT BREAK (%) +10/-20 +10/-20
VOLUME SWELL: AT 70°C for 72hrs ASTM D471
In IRM OIL NO 901 +18% +18%
In IRM OIL NO 902 23% +23%
In IRM OIL NO 903 +60% +60%
CHEMICAL RESISTANCE
— OZONE (50 PPHM /20 DEG / 100HRS) PASSED ASTM D1149 NO CRACKS
— DILUTE ACIDS AND BASES GOOD GOOD
— CONCENTRATED ACIDS AND BASES FAIR FAIR
— OILS GOOD GOOD
— SOLVENTS FAIR FAIR
TEMPERATURE RANGE -30 to +100ºC -30 to +100ºC
FIRE & SMOKE
FIRE – CLASSIFICATION NF F16-101 MEETS M2 REQUIREMENT NFF 16-101 MEETS M2 REQUIREMENT
SMOKE CLASSIFICATION
SMOKE DENSITY NF F16-101 MEETS F3 REQUIREMENT
SMOKE TOXICITY NF F16-101 MEETS F3 REQUIREMENT
UL94 VO PASS
COLOUR BLACK
Download Data Sheet
Characteristics Values
Specific Gravity 1.20
Hardness (o Shore A) 60 ± 5
Tensile Strength, (Kgf/cm2), min 80
Elongation At Break, (%), min 250
Maximum compression set after 24h at 70oC, (%) 25
Flame resistance (according to ISO 340) Flame persistence (after removing the burner) Max 45s
The flame mustn’t reappear after an air draughtiness application Max 15
Antistatic characteristic (according to BS 490) Surface electrical resistance (Ω), max 3 x 108
Temperature Range -30o to +100oC
Compression Set (70oC for 22 hours), (%) 25
Polymer Content Blend
View Material ProductDownload Data Sheet
  • INTERNATIONAL MARITIME ORGANISATION (IMO) FTP CODE PART 5/ISO 5658-2:2006
  • Flame Retardant Neoprene Gasket
  • 70° shore hardness
  • CE, PAH, RoHS & REACh compliant
PROPERTIES TEST METHOD VALUES TEST METHOD VALUES
FPS UNITS METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.60 ± 0.05 ASTM D297 1.60 ± 0.05
HARDNESS DIN 53505 70 ± 5 Sh A ASTM D2240 70 ± 5 Sh A
TENSILE STRENGTH ( min ) DIN 53504 994 PSI ASTM D412 70 kg/cm2
ELONGATION AT BREAK ( min ) DIN 53504 300% ASTM D412 300%
COMPRESSION SET (70ºC/24  hrs/25% set) (max) DIN 53517 40% ASTM D395 METHOD B 40%
TEAR RESISTANCE (Angular) min DIN 53515 335 Lbs/Inch ASTM D624 30 Kg/cm
CHANGE IN PROPERTIES
HEAT AGEING (72 hrs. AT 70ºC ) ASTM D573
— HARDNESS (Pts) + 5 (Max) + 5 (Max)
— TENSILE STRENGTH (%) + 15 / -15 + 15 / -15
— ELONGATION AT BREAK (%) – 40 – 40
POLYMER 100 % NEOPRENE 100 % NEOPRENE
 OZONE RESISTANCE 100 PPHM 72 H 40ºC 30 % Strain NO CRACKS ASTM D 1149 NO CRACKS
CHANGE IN VOLUME (ASTM oil No.3/70 ºC/70 hrs) (%)(MAX))) ASTM D471 45%
DI-ELECTRIC STRENGTH OF INSULATING MATERIALS (Kv/mm) (MIN) CEI EN 60243-2 10
TEST FOR SURFACE FLAMMABILITY, REACTION TO FIRE TESTS – SPREAD OF FLAME IMO FTP CODE PART-5/ ISO 565-2:2006
–CRITICAL FLUX AT EXTINGUISHMENT (CFE), Kw/m2 ( ≥7.0) PASS
–HEAT FOR SUITABLE BURNING (Qsb), MJ/m2 (≥0.25) PASS
–TOTAL HEAT RELEASED (Qt), MJ (≥2.0) PASS
–PEAK HEAT RELEASE RATE (Qp), kW (≥ 10.0) PASS
TEMPERATURE RANGE -30º to + 100ºC -30º to + 100ºC
COLOUR GREY GREY
View Material ProductDownload Data Sheet
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.45 ± 0.05 ASTM D297 1.45 ± 0.05
HARDNESS DIN 53505 50 ± 5 SH A ASTM D2240 50 ± 5 SH A
TENSILE STRENGTH (MIN) DIN 53504 569 PSI ASTM D412 40 KG/CM2
ELONGATION AT BREAK (MIN) DIN 53504 200% ASTM D412 200%
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) DIN ISO 815-1 40% ASTM D395 METHOD B 40%
TEAR RESISTANCE (ANGULAR) MIN DIN 53515 100 LBS/INCH ASTM D624 18 KG/CM
CHANGE IN PROPERTIES
HEAT AGEING (72 HRS. AT 70ºC) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 25 + 10 / – 25
— ELONGATION AT BREAK (%) + 10 / – 25 + 10 / – 25
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 + 33% + 33%
IRM OIL NO.2 + 47% + 47%
IRM OIL NO.3 + 90% + 90%
POLYMER CONTENT (NEOPRENE) 10% 10%
CHEMICAL RESISTANCE
— OZONE FAIR ASTM D 1149 FAIR
— DILUTE ACIDS AND BASES FAIR FAIR
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED NOT RECOMMENDED
— OILS NOT RECOMMENDED NOT RECOMMENDED
— SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE -30 º TO +90º C -30 º TO +90º C
COLOUR BLACK
View Material ProductDownload Data Sheet
  • REACH, RoHS, PAH and CE compliant
  • Certified to BS2752 C80
  • Neoprene: 80° Shore
  • Meets ASTM D 2000 M3 BC713A14B14EF11G21Z
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.50
HARDNESS BS 903: PART A26 80 + 5-4 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 133
ELONGATION AT BREAK (MIN) BS 903: PART A2 100%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 25%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 45 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 60% (MAX)
RESISTANCE TO LOW TEMPERATURE AT –

40ºC

 BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC &

NAPHTHANIC HC

 GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +60
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • REACH, RoHS, PAH and CE compliant
  • Certified to BS2752 C70
  • Neoprene: 70° Shore
  • Meets ASTM D 2000 M3 BC713A14B14EF11G21Z
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.40
HARDNESS BS 903: PART A26 70 + 5-4 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 133
ELONGATION AT BREAK (MIN) BS 903: PART A2 200%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 25%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 40 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 70% (MAX)
RESISTANCE TO LOW TEMPERATURE AT –

30ºC

 BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC &

NAPHTHANIC HC

 GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +70
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • REACH, RoHS, PAH and CE compliant
  • Certified to BS2752 C60
  • Neoprene: 60˚ Shore
  • Meets ASTM D 2000 M3 BC613A14B14EF11G21Z
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.40
HARDNESS BS 903: PART A26 60 + 5-4 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 133
ELONGATION AT BREAK (MIN) BS 903: PART A2 250%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 25%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 35 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 70% (MAX)
RESISTANCE TO LOW TEMPERATURE AT –

30ºC

 BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC &

NAPHTHANIC HC

 GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +70
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • Certified to BS2752
  • REACH, RoHS, PAH and CE compliant
  • Neoprene: 50° Shore
  • Meets ASTM D 2000 M3 BC512A14B14EF11G21Z
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.35
HARDNESS BS 903: PART A26 50 + 5-4 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 123
ELONGATION AT BREAK (MIN) BS 903: PART A2 400%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 30%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 30 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 80% (MAX)
RESISTANCE TO LOW TEMPERATURE AT – 40ºC BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC & NAPHTHANIC HC GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +80
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • Certified to BS2752 C40
  • REACH, RoHS, PAH and CE compliant
  • Neoprene: 40° Shore
  • Meets ASTM D 2000 M3 BC409A14B14EF11G21Z
PROPERTIES TEST METHOD VALUES
METRIC UNITS
SPECIFIC GRAVITY BS 903: PART A1 1.25
HARDNESS BS 903: PART A26 40 + 5-4 IRHD
TENSILE STRENGTH (KG/CM2) BS 903:  PART A2 92
ELONGATION AT BREAK (MIN) BS 903: PART A2 450%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) BS 903: PART A6 30%
TEAR RESISTANCE ( ANGULAR ) MIN BS 903:  PART A3 25 Kg/cm
RESISTANCE TO ACCELERATED AGEING- 168HRS AT 70˚C BS 903: PART A19
— HARDNESS (Pts) BS 903: PART A26 + 7 (MAX)
— TENSILE STRENGTH (%) BS 903: PART A2 -12 (MAX)
— ELONGATION AT BREAK (%) BS 903: PART A2 -20 (MAX)
VOLUME SWELL: AT 40˚C FOR 24 HRS/IN BS 903: PART A16
FUEL B + 100% (MAX)
RESISTANCE TO LOW TEMPERATURE AT – 40ºC BS 903: PART A13 MEETS REQUIREMENTS
ADHESION TO AND CORROSION OF METALS BS 903: PART A 37 MEETS REQUIREMENTS
POLYMER CONTENT (NEOPRENE) 100%
ADDITIONAL INFORMATION –
CHEMICAL RESISTANCE
— OZONE BS 903: PART A 43 GOOD
— DILUTE ACIDS AND BASES BS 903: PART A16 GOOD
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED
— MINERAL OILS – PARAFINNIC & NAPHTHANIC HC GOOD
— MINERAL OILS – AROMATIC HC FAIR
–ANIMAL/VEGETABLE OIL GOOD
–SOLVENTS FAIR
TEMPERATURE RANGE -30º TO + 120º C
COLOUR BLACK
VOLUME SWELL DATA
RESISTANCE TO LIQUIDS BS ISO 1817, 24 h at (40±1) °C -0
VOLUME CHANGE (%) AFTER IMMERSION IN LIQUID B BS ISO 1817, 24 h at (40±1) °C +100
RESISTANCE TO ACCELERATED AGEING PART A19, AIR-OVEN METHOD A, (168±2)h, (70±1)°C -0
CHANGE IN HARDNESS DEGREES (IRHD) PART A26, METHOD N, MEASUREMENTS BEFORE AND AFTER AGEING ON THE SAME 2 PLIES EACH 2.00MM THICK +7
MAXIMUM CHANGE IN TENSILE STRENGTH (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -12
MAXIMUM CHANGE IN ELONGATION AT BREAK (% OF ORIGINAL VALUE) PART A2, TYPE 1 OR TYPE 2 DUMBBELLS -20
View Material ProductDownload Data Sheet
  • Approved to FDA 21 CFR 177.2600 – EU1935/2004 Compliant
  • REACH, RoHS, PAH and CE compliant
  • Metal Detectable Neoprene: 65° Shore
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.50 ± 0.05 ASTM D297 1.50 ± 0.05
HARDNESS DIN 53505 65 ± 5 SH A ASTM D2240 65 ± 5 SH A
TENSILE STRENGTH ( MIN ) DIN 53504 1990PSI ASTM D412 140 KG/CM2
ELONGATION AT BREAK ( MIN ) DIN 53504 600% ASTM D412 600%
COMPRESSION SET (70ºC/24 HRS/25% SET) (MAX) DIN 53517 50% ASTM D395 METHOD B 50%
POLYMER CONTENT (%) 100 100
TEAR RESISTANCE ( ANGULAR ) MIN DIN 53515 170 LBS/INCH ASTM D624 30 KG/CM
CHANGE IN PROPERTIES AFTER
HEAT AGEING ( 72 HRS. AT 70 ºC ) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 25 + 10 / – 25
— ELONGATION AT BREAK (%) + 10 / – 30 + 10 / – 30
VOLUME SWELL : AT 70ºC FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 +18% +18%
IRM OIL NO.2 +23% +23%
IRM OIL NO.3 +60% +60%
POLYMER CONTENT (NEOPRENE) 100% 100%
CHEMICAL RESISTANCE
— OZONE GOOD ASTM D 1149 GOOD
— DILUTE ACIDS AND BASES GOOD GOOD
— CONCENTRATED ACIDS AND BASES FAIR FAIR
— OILS GOOD GOOD
— SOLVENTS FAIR FAIR
TEMPERATURE RANGE -25º TO + 120º C -25º TO + 120º C
COLOUR BLUE
Download Data Sheet
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.45 ± 0.05 ASTM D297 1.45 ± 0.05
HARDNESS DIN 53505 70 ± 5 SH A ASTM D2240 70 ± 5 SH A
TENSILE STRENGTH (MIN) DIN 53504 858 PSI ASTM D412 50 KG/CM2
ELONGATION AT BREAK (MIN) DIN 53504 250% ASTM D412 250%
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) DIN 53517 50% ASTM D395 METHOD B 50%
TEAR RESISTANCE (ANGULAR) MIN DIN 53515 84 LBS/INCH ASTM D624 15 KG/CM
CHANGE IN PROPERTIES
HEAT AGEING (72 HRS. AT 70 ºC) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) ± 20% (MAX) ± 20% (MAX)
— ELONGATION AT BREAK (%) ± 30% (MAX) ± 30% (MAX)
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 18% 19%
IRM OIL NO.2 37% 37%
IRM OIL NO.3 72% 72%
POLYMER CONTENT (NEOPRENE) 30% 30%
CHEMICAL RESISTANCE
— OZONE FAIR ASTM D 1149 FAIR
— DILUTE ACIDS AND BASES GOOD GOOD
— CONCENTRATED ACIDS AND BASES FAIR FAIR
— OILS FAIR FAIR
— SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE -30 º TO +90º C -30 º TO +90º C
COLOUR BLACK
View Material ProductDownload Data Sheet
  • Meets ASTM D 2000 M3 BC604A14B14EO34G21
  • REACH, RoHS, PAH and CE compliant
  • An excellent economy option
  • Neoprene/SBR rubber: 70° Shore
PROPERTIES TEST METHOD VALUES FPS UNITS TEST METHOD VALUES METRIC UNITS
SPECIFIC GRAVITY DIN 53508 1.50 ± 0.05 ASTM D297 1.70 ± 0.05
HARDNESS DIN 53505 70 ± 5 SH A ASTM D2240 70 ± 5 SH A
TENSILE STRENGTH (MIN) DIN 53504 497 PSI ASTM D412 35 KG/CM2
ELONGATION AT BREAK (MIN) DIN 53504 200% ASTM D412 200%
COMPRESSION SET (70 ºC/24 HRS/25% SET) (MAX) DIN 53517 50% ASTM D395 METHOD B 50%
TEAR RESISTANCE (ANGULAR) MIN DIN 53515 84 LBS/INCH ASTM D624 15 KG/CM
CHANGE IN PROPERTIES
HEAT AGEING (72 HRS. AT 70 ºC) ASTM D573
— HARDNESS (PTS) + 5 (MAX) + 5 (MAX)
— TENSILE STRENGTH (%) + 10 / – 25 + 10 / – 25
— ELONGATION AT BREAK (%) + 10 / – 25 + 10 / – 25
VOLUME SWELL : AT 70º C FOR 72 HRS/IN ASTM D 471
IRM OIL NO.1 + 33% + 33%
IRM OIL NO.2 + 47% + 47%
IRM OIL NO.3 + 90% + 90%
POLYMER CONTENT (NEOPRENE) 10% 10%
CHEMICAL RESISTANCE
— OZONE FAIR ASTM D 1149 FAIR
— DILUTE ACIDS AND BASES FAIR FAIR
— CONCENTRATED ACIDS AND BASES NOT RECOMMENDED NOT RECOMMENDED
— OILS NOT RECOMMENDED NOT RECOMMENDED
— SOLVENTS NOT RECOMMENDED NOT RECOMMENDED
TEMPERATURE RANGE -30 º TO +70º C -30 º TO +70º C
COLOUR BLACK